LITHIUM-ION SEPARATOR INCIMENTUM CUMATIUM EXSTRUCTIO
PVDF Copolymer resinae productus est copolymer pulveris vel particula polyvinylidene fluoride formata.Ob praesentiam comonomers, PVDF non solum habet bonam vim mechanicam, resistentiam chemicam, resistentiam senescentem et alias proprietates, sed etiam bonam flexibilitatem et punctum liquationis humilem, lt applicari potest ad PVDF agros processus productos ut iniectio fingens et extrusio; et adhiberi potest etiam ad tunicas ut separatores lithium altilium.
Technical Indexs
| Item | Unitas | DS2026-01 | DS2026-02 | Test Methodi / Standards |
| Aspectus | / | Alba potentia | Alba potentia / particula | Visual inspectionem |
| Magnitudo particula D50 | μm | 10±5 | / | GB/T 19077.1 |
| Densitas relativa | g/cm3 | 1.76-7.78 | 1.76-1.78 | GB/T 1033.1 |
| Liquescens punctum | ℃ | 155±5 | 155±5 | ASTM D4441 |
| Humorem content | % | ≤0.1 | ≤0.1 | GB/T 6284 |
| Scelerisque Decomposition Temperature | ℃ | ≥380 | ≥380 | GB/T 33047 |
| O Rate conflandum | g/10min | ≤4.0 | 4.0-25.0 | ASTM D1238,230°C/12.5kg |
| Rotatione Viscositas | mpa.s | 500-4000 | / | 25°C 0.lg/g NMP |
| Distrahentes fortitudo | MPa | ≥35 | ≥35 | GB/T 1040 |
| Prolongatio Rate | % | ≥25 | ≥25 | GB/T 1040 |
Applicationem
1.DS2026-01 Maxime ad lithium altilium saeptum membranae adhibitae, et oleum substructum et aquaticum in tunicis uti possunt.
2.DS2026-02 Praeparatio productorum PVDF per fingum, extrusionem et alios processus processus.
Operam
Temperatus processus non debet 350°C excedere, ad vitandam compositionem et generationem vaporum toxicorum.
Sarcina, translationem ac at
1. Sarcinis in plastic saccis et tympanis in charta collocatis, cum rete contentum 20Kg per tympanum.
2. Productum ex non periculoso productum deportatur.
3. In ambitu mundissimo et sicco 5-30 condi debet, ne sordes ut pulvis et vaporum aqua misceantur.