Alta frequentia et humilis dielectric FEP（DS618HD）
Princeps frequentia et humilis dielectric FEP est copolymer tetrafluoroethylene (TFE) et
hexafluoropropylene (HFP), quae melius dielectricae detrimentum in altum cum frequentiis altis habet, bonum
scelerisque stabilitas, inertia chemica praestans, humilis frictio coefficiens et excellentia
electrica velit.Per methodum thermoplasticam discursum esse potest.
Technical Indexs
| Item | Unitas | DS618HD | Test Methodi / Standards |
| Aspectus | / | Translucens particula visibili-nigrae recipis punctum minus quam I% | HG/T 2904 |
| Index liquefactionem | g/10min | 20-42 | GB/T 2410 |
| Distrahentes fortitudo | Mpa | ≥21.0 | GB/T 1040 |
| Prolongatio ad intermissum | % | ≥320 | GB/T 1040 |
| Gravitas relativa | / | 2.12-2.17 | GB/T 1033 |
| Liquescens punctum | ℃ | 260±10 | GB/T 19466.3 |
| Dielectric Constant (1 MHz) | / | 2.10 | GB/T 1409 |
| Dielectric Factor (1MHz) | / | 4.0×10-4 | GB/T 1409 |
| Dielectric Constant (2.45 GHz) | / | 2.10 | GB/T 1409 |
| Dielectric Factor (2.45 GHz) | / | 4.0×10-4 | GB/T 1409 |
| Dielectric Constant (10 GHz) | / | ≤2.05 | GB/T 1409 |
| Dielectric Factor (10 GHz) | / | 4.0×10-4 | GB/T 1409 |
Applicationem
Maxime in communicationis, navigationis, medicinae, navigationis, 5G, electronici et electrici, et aliorum agrorum, praesertim cum summus celeritas extrutionis materiarum parvarum caliberwire velitarum adhibita est, etiam proprietates dielectricas optimas habet et resistentiam crepuit dum alta celeritate extrusionem occurrens
Operam
Temperatura processus non excedere debet 420 , ad vitandam compositionem et generationem vaporum toxicorum.
Sarcina, translationem ac at
1.Packed in plastic saccis, rete pondus 25kg per sacculum.
2. Productum ex non periculoso productum deportatur.
3. In mundis, siccis, frigidis et obscuris ambitus conservatis, contaminationem devita.